Descripción
DIP Zirconia Blanks are high-quality, multi-layered round disks designed for superior color gradient and anterior translucency. They offer exceptional stability and durability for constructing all types of bridge frameworks, with high flexural strength to prevent split-offs. Ideal for use in highly aesthetic areas, these blanks provide durable, long-lasting, and predictable results. They are perfect for creating veneers, inlays/onlays, and both posterior and anterior crowns and bridges using CAD/CAM technology.
In addition, DIP Zirconia Blanks are fully biocompatible, ensuring they are well-tolerated by the human body without causing allergic reactions. With proper care, zirconia restorations can last many years, even decades, making them not only aesthetically pleasing but also a cost-effective, long-term solution.
Indications:
- Veneers
- Inlays/Onlays
- Posterior crowns
- Anterior crowns
- Bridges (both posterior and anterior)
- Bridge frameworks
Features & Benefits:
- Natural aesthetics - Multi-layered color gradient provides a natural, lifelike appearance
- High translucency - Superior translucency is ideal for anterior restorations, ensuring a seamless blend with natural teeth
- Exceptional durability - High stability and resilience make them suitable for all types of dental bridge frameworks
- High flexural strength - Robust against splits and fractures, ensuring longevity and reliability
- Ideal for aesthetic zones - Perfect for use in highly visible areas due to their superior aesthetic qualities
- Biocompatible - Fully biocompatible and well-tolerated by the human body, minimizing the risk of allergic reactions
- Long-lasting - With proper care, zirconia restorations can endure for many years, often lasting decades
- Cost-effective - Offers a long-term, durable solution, reducing the need for frequent replacements and associated costs
- Versatile - Suitable for various dental applications, including veneers, inlays/onlays, crowns, and bridges, enhancing their utility in dental practices
Technical Information:
- Translucency: 43-46.6%
- Bending strength: 1300-1027 MPa
- Density after sintering: ≥6.0g/cm³
- Fracture toughness: 4.3-5.1 MPa•m
- Sintering temperature: 1480°С (recommend)
- CTE: (25-500°С) (10.5±1.0) x 10 -6 K-1
- Accelerated aging surface monoclinic phase content: <5%
- Chemical solubility after sintering: <100μg/cm2
- Size: round block Ø98mm
Package includes 1 zirconia block - shade and thickness are for selection